Electrical tracking resistance compositions, articles formed therefrom, and methods of manufacture thereof

ABSTRACT

A composition comprises, based on the total weight of the composition, 45 wt % to 75 wt % of a polyetherimide; and 20 wt % to 45 wt % of talc; and 5 wt % to 15 wt % of a fluorinated polymer; wherein the composition has a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85.

BACKGROUND

This disclosure is directed to polyetherimide compositions, and in particular to electrical tracking resistant polyetherimide compositions, articles formed therefrom, and their methods of manufacture.

Polyetherimides are known as outstanding high performance materials, having a high glass transition temperature (Tg), high modulus, and strength at elevated temperatures, as well as excellent chemical resistance. They are useful in the manufacture of articles and components for a wide range of applications. Because of their broad use, particularly in the electrical and electronic industries, it is desirable to provide polyetherimides with good electrical tracking resistance. Electrical tracking is the formation of conductive pathways on the surface of a polymer under certain conditions and at a certain voltage. Electrical tracking in a polymer can be a source of fire in parts therefore resistance to electrical tracking is often an important safety requirement for a material used in certain electrical applications. A common method of reporting the electrical tracking resistance of a polymer is by its comparative tracking index rating (CTI). Currently known polyetherimides can have a comparative tracking index (CTI) of 100 to 175 volts. However, some applications can require a material having a higher CTI.

There accordingly remains a need in the art for polyetherimide compositions that have excellent electrical tracking resistance. It would be a further advantage if the compositions could be rendered electrical tracking resistant without a significant detrimental effect on one or more of material cost, processability, and mechanical properties.

SUMMARY

The above-described and other deficiencies of the art are met by a polyetherimide composition comprising: based on the total weight of the composition, 45 wt % to 75 wt % of a polyetherimide; and 20 wt % to 45 wt % of talc; and 5 wt % to 15 wt % of a fluorinated polymer; wherein the composition has a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85.

In another embodiment, a method of manufacture comprises combining the above-described components to form a polyetherimide composition.

In yet another embodiment, an article comprises the above-described polyetherimide composition.

In still another embodiment, a method of manufacture of an article comprises molding, extruding, or shaping the above-described polyetherimide composition into an article.

The above described and other features are exemplified by the following drawings, detailed description, examples, and claims.

DETAILED DESCRIPTION

The inventors have discovered that the addition of 20 wt % to 45 wt % of talc, and 5 to 25 wt % of a fluorinated polymer to polyetherimides results in a significant improvement in the electrical tracking resistance of the polyetherimides. The inventors have also discovered that the addition of 20 wt % to 45 wt % of talc, and 5 to 25 wt % of a fluorinated polymer to polyetherimides provides compositions having balanced mechanical properties.

Polyetherimides comprise more than 1, for example 2 to 1000, or 5 to 500, or 10 to 100 structural units of formula (1)

wherein each R is independently the same or different, and is a substituted or unsubstituted divalent organic group, such as a substituted or unsubstituted C₆₋₂₀ aromatic hydrocarbon group, a substituted or unsubstituted straight or branched chain C₂₋₂₀ alkylene group, a substituted or unsubstituted C₃₋₈ cycloalkylene group, in particular a halogenated derivative of any of the foregoing. In some embodiments R is divalent group of one or more of the following formulas (2)

wherein Q¹ is —O—, —S—, —C(O)—, —SO₂—, —SO—, —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (which includes perfluoroalkylene groups), or —(C₆H₁₀)_(z)— wherein z is an integer from 1 to 4. In some embodiments R is m-phenylene, p-phenylene, or a diarylene sulfone, in particular bis(4,4′-phenylene)sulfone, bis(3,4′-phenylene)sulfone, bis(3,3′-phenylene)sulfone, or a combination comprising at least one of the foregoing. In some embodiments, at least 10 mole percent of the R groups contain sulfone groups, and in other embodiments no R groups contain sulfone groups.

Further in formula (1), T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions, and Z is an aromatic C₆₋₂₄ monocyclic or polycyclic moiety optionally substituted with 1 to 6 C₁₋₈ alkyl groups, 1 to 8 halogen atoms, or a combination comprising at least one of the foregoing, provided that the valence of Z is not exceeded. Exemplary groups Z include groups of formula (3)

wherein R^(a) and R^(b) are each independently the same or different, and are a halogen atom or a monovalent C₁₋₆ alkyl group, for example; p and q are each independently integers of 0 to 4; c is 0 to 4; and X^(a) is a bridging group connecting the hydroxy-substituted aromatic groups, where the bridging group and the hydroxy substituent of each C₆ arylene group are disposed ortho, meta, or para (specifically para) to each other on the C₆ arylene group. The bridging group X^(a) can be a single bond, —O—, —S—, —S(O)—, —S(O)₂—, —C(O)—, or a C₁₋₁₈ organic bridging group. The C₁₋₁₈ organic bridging group can be cyclic or acyclic, aromatic or non-aromatic, and can further comprise heteroatoms such as halogens, oxygen, nitrogen, sulfur, silicon, or phosphorous. The C₁₋₁₈ organic group can be disposed such that the C₆ arylene groups connected thereto are each connected to a common alkylidene carbon or to different carbons of the C₁₋₁₈ organic bridging group. A specific example of a group Z is a divalent group of formula (3a)

wherein Q is —O—, —S—, —C(O)—, —SO₂—, —SO—, or —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (including a perfluoroalkylene group). In a specific embodiment Z is a derived from bisphenol A, such that Q in formula (3a) is 2,2-isopropylidene.

In an embodiment in formula (1), R is m-phenylene, p-phenylene, or a combination comprising at least one of the foregoing, and T is —O—Z—O— wherein Z is a divalent group of formula (3a). Alternatively, R is m-phenylene, p-phenylene, or a combination comprising at least one of the foregoing, and T is —O—Z—O wherein Z is a divalent group of formula (3a) and Q is 2,2-isopropylidene. Alternatively, the polyetherimide can be a copolymer comprising additional structural polyetherimide units of formula (1) wherein at least 50 mole percent (mol %) of the R groups are bis(3,4′-phenylene)sulfone, bis(3,3′-phenylene)sulfone, or a combination comprising at least one of the foregoing and the remaining R groups are p-phenylene, m-phenylene or a combination comprising at least one of the foregoing; and Z is 2,2-(4-phenylene)isopropylidene, i.e., a bisphenol A moiety.

In some embodiments, the polyetherimide is a copolymer that optionally comprises additional structural imide units that are not polyetherimide units, for example imide units of formula (4)

wherein R is as described in formula (1) and each V is the same or different, and is a substituted or unsubstituted C₆₋₂₀ aromatic hydrocarbon group, for example a tetravalent linker of the formulas

wherein W is a single bond, —S—, —C(O)—, —SO₂—, —SO—, or —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (which includes perfluoroalkylene groups). These additional structural imide units preferably comprise less than 20 mol % of the total number of units, and more preferably can be present in amounts of 0 to 10 mol % of the total number of units, or 0 to 5 mol % of the total number of units, or 0 to 2 mole % of the total number of units. In some embodiments, no additional imide units are present in the polyetherimide.

The polyetherimide can be prepared by any of the methods known to those skilled in the art, including the reaction of an aromatic bis(ether anhydride) of formula (5) or a chemical equivalent thereof, with an organic diamine of formula (6)

wherein T and R are defined as described above. Copolymers of the polyetherimides can be manufactured using a combination of an aromatic bis(ether anhydride) of formula (5) and an additional bis(anhydride) that is not a bis(ether anhydride), for example pyromellitic dianhydride or bis(3,4-dicarboxyphenyl) sulfone dianhydride.

Illustrative examples of aromatic bis(ether anhydride)s include 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride (also known as bisphenol A dianhydride or BPADA), 3,3-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfone dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl-2,2-propane dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-(hexafluoroisopropylidene)diphthalic anhydride; and 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride. A combination of different aromatic bis(ether anhydride)s can be used.

Examples of organic diamines include 1,4-butane diamine, 1,5-pentanediamine, 1,6-hexanediamine, 1,7-heptanediamine, 1,8-octanediamine, 1,9-nonanediamine, 1,10-decanediamine, 1,12-dodecanediamine, 1,18-octadecanediamine, 3-methylheptamethylenediamine, 4,4-dimethylheptamethylenediamine, 4-methylnonamethylenediamine, 5-methylnonamethylenediamine, 2,5-dimethylhexamethylenediamine, 2,5-dimethylheptamethylenediamine, 2,2-dimethylpropylenediamine, N-methyl-bis (3-aminopropyl) amine, 3-methoxyhexamethylenediamine, 1,2-bis(3-aminopropoxy) ethane, bis(3-aminopropyl) sulfide, 1,4-cyclohexanediamine, bis-(4-aminocyclohexyl) methane, m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diaminotoluene, m-xylylenediamine, p-xylylenediamine, 2-methyl-4,6-diethyl-1,3-phenylene-diamine, 5-methyl-4,6-diethyl-1,3-phenylene-diamine, benzidine, 3,3′-dimethylbenzidine, 3,3′-dimethoxybenzidine, 1,5-diaminonaphthalene, bis(4-aminophenyl) methane, bis(2-chloro-4-amino-3,5-diethylphenyl) methane, bis(4-aminophenyl) propane, 2,4-bis(p-amino-t-butyl) toluene, bis(p-amino-t-butylphenyl) ether, bis(p-methyl-o-aminophenyl) benzene, bis(p-methyl-o-aminopentyl) benzene, 1,3-diamino-4-isopropylbenzene, bis(4-aminophenyl) sulfide, bis-(4-aminophenyl) sulfone (also known as 4,4′-diaminodiphenyl sulfone (DDS)), and bis(4-aminophenyl) ether. Any regioisomer of the foregoing compounds can be used. C₁₋₄ alkylated or poly(C₁₋₄)alkylated derivatives of any of the foregoing can be used, for example a polymethylated 1,6-hexanediamine. Combinations of these compounds can also be used. In some embodiments the organic diamine is m-phenylenediamine, p-phenylenediamine, 4,4′-diaminodiphenyl sulfone, 3,4′-diaminodiphenyl sulfone, 3,3′-diaminodiphenyl sulfone, or a combination comprising at least one of the foregoing.

The polyetherimides can have a melt index of 0.1 to 10 grams per minute (g/min), as measured by American Society for Testing Materials (ASTM) D1238 at 340 to 370° C., using a 6.7 kilogram (kg) weight. In some embodiments, the polyetherimide has a weight average molecular weight (Mw) of 1,000 to 150,000 grams/mole (Dalton), as measured by gel permeation chromatography, using polystyrene standards. In some embodiments the polyetherimide has an Mw of 10,000 to 80,000 Daltons. Such polyetherimides typically have an intrinsic viscosity greater than 0.2 deciliters per gram (dl/g), or, more specifically, 0.35 to 0.7 dl/g as measured in m-cresol at 25° C.

The amount of polyetherimide used in the polyetherimide compositions can vary widely, and is that amount effective to provide the desired mechanical properties and electrical tracking resistance. In some instances the polyetherimide is present in an amount from 50 wt % to 90 wt %, specifically 50 wt % to 80 wt %, and more specifically 50 wt % to 70 wt %, each based on the total weight of the polyetherimide compositions.

Talc has been surprisingly found as a useful additive for improving electrical tracking resistance performance of polyetherimide particularly in the presence of a floriated polymer. The amount of talc is in the range of 20 to 45 wt. %, or 25 to 45 wt %, or in the range of 35 to 45 wt %, based on the total weight of the polyetherimide compositions.

The particle size of talc can affect the CTI performance of the polyetherimide compositions. In some embodiments, the titanium dioxide has a D95 of 2 microns to 6 microns. As used herein, D95 refer to the cut-particle diameter of the particulate where 95 wt % of the particles in the total distribution of the referenced sample have the noted particle diameter or smaller. For example, a D95 particle size of 3.5 microns means that 95 wt % of the particles in the sample have a diameter of 3.5 microns or less. In some embodiments, the particle size is determined by sedigraph analysis using for example a Micromeritics Sedigraph 5120 Particle Size Analysis System.

The polyetherimide compositions further includes a fluoropolymer. “Fluoropolymers” as used herein include homopolymers and copolymers that comprise repeating units derived from a fluorinated alpha-olefin monomer, i.e., an alpha-olefin monomer that includes at least one fluorine atom substituent, and optionally, a non-fluorinated, ethylenically unsaturated monomer reactive with the fluorinated alpha-olefin monomer. Exemplary fluorinated alpha-olefin monomers include, but are not limited to, CF₂═CF₂, CHF═CF₂, CH₂═CF₂, CH₂═CHF, CClF═CF₂, CCl₂═CF₂, CClF═CClF, CHF═CCl₂, CH₂═CClF, and CCl₂═CClF, CF₃CF═CF₂, CF₃CF═CHF, CF₃CH═CF₂, CF₃CH═CH₂, CF₃CF═CHF, CHF₂CH═CHF, and CF₃CH═CH₂. Specifically, the fluorinated alpha-olefin monomer is one or more of tetrafluoroethylene (CF₂═CF₂), chlorotrifluoroethylene (CClF═CF₂), vinylidene fluoride (CH₂═CF₂), and hexafluoropropylene (CF₂═CFCF₃). Exemplary non-fluorinated monoethylenically unsaturated monomers include, but are not limited to, ethylene, propylene, butene, (meth)acrylate monomers such as methyl methacrylate and butyl acrylate, ethylenically unsaturated aromatic monomers such as styrene, vinyl ethers such as cyclohexyl vinyl ether, ethyl vinyl ether, and n-butyl vinyl ether, and vinyl esters such as vinyl acetate and vinyl versatate. Exemplary fluoropolymers include, but are not limited to, poly(tetrafluoroethylene) homopolymer (PTFE), poly(hexafluoroethylene), poly(tetrafluoroethylene-hexafluoroethylene), and poly(tetrafluoroethylene-ethylene-propylene). A specific exemplary fluoropolymer is PTFE, which can be fibril forming or non-fibril forming.

The fluoropolymer can be associated with, e.g., encapsulated by, another copolymer, for example a copolymer including units derived from the non-fluorinated ethylenically unsaturated monomers above and others. In some embodiments, the copolymer is a rigid copolymer such as styrene-acrylonitrile copolymer (SAN). PTFE encapsulated in SAN is known as TSAN. An exemplary TSAN includes 25 to 75 wt %, specifically 50 wt % PTFE and 25 to 75 wt %, specifically 50 wt % SAN, based on the total weight of the encapsulated fluoropolymer. The SAN can include, for example, 75 wt % styrene and 25 wt % acrylonitrile based on the total weight of the copolymer.

One fluoropolymer composition that can be used in the instant compositions is commercially available from 3M under the trade name 3M Dyneon® MM 5935EF, and is particularly effective for formulating compositions that can attain a combination of good flame retardance, low smoke density, and low heat release, when used together with the aromatic polycarbonate, polyetherimide, and optionally sodium trichlorobenzene sulphonate disclosed herein.

The polyetherimide compositions can include various additives ordinarily incorporated into polymer compositions of this type, with the proviso that the additives are selected so as to not significantly adversely affect the desired properties of the composition. Exemplary additives include catalysts, impact modifiers, fillers, antioxidants, thermal stabilizers, light stabilizers, ultraviolet light (UV) absorbing additives, quenchers, plasticizers, lubricants, mold release agents, antistatic agents, visual effect additives such as dyes, pigments, and light effect additives, flame retardants, anti-drip agents, and radiation stabilizers. Combinations of additives can be used, for example a combination of a heat stabilizer, a mold release agent, and optionally an ultraviolet light stabilizer. In some embodiments the polyetherimide compositions further comprise an additive selected from a processing aid, a heat stabilizer, an ultraviolet light absorber, a colorant, a flame retardant, or a combination comprising at least one of the foregoing. In general, the additives are used in the amounts generally known to be effective. The foregoing additives (except any fillers) are generally present in an amount of 0.0001 to 20 wt % or 0.005 to 20 wt %, specifically 0.01 to 10 wt %, based on the total weight of the composition. Alternatively, in some embodiments, the compositions do not contain appreciable amounts of additives, and in some embodiments, there are no detectable amounts of additives, i.e., additives are substantially absent or absent from the compositions. Accordingly, the foregoing additives (except any fillers) can be present in an amount from 0 to 0.1 wt %, 0 to 0.01 wt %, 0 to 0.001 wt %, or 0 to 0.0001 wt %, based on the total weight of the composition. In another embodiment, no appreciable amount of any additive other than a heat stabilizer, a mold release agent, and optionally an ultraviolet light stabilizer is present in the compositions. In still another embodiment, no detectable amount of any additive other than a heat stabilizer, a mold release agent, and optionally an ultraviolet light stabilizer is present in the compositions.

Suitable antioxidants can be compounds such as phosphites, phosphonites and hindered phenols or a combination comprising at least one of the foregoing antioxidants. Phosphorus-containing stabilizers including triaryl phosphites and aryl phosphonates are useful additives. Difunctional phosphorus containing compounds can also be unseeded. Preferred stabilizers can have a molecular weight greater than 300. Some exemplary compounds are tris-di-tert-butylphenyl phosphite available from Ciba Chemical Co. as IRGAFOS 168 and bis (2,4-dicumylphenyl) pentaerythritol diphosphite available commercially from Dover Chemical Co. as DOVERPHOS S-9228.

Examples of phosphites and phosphonites include: triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)-pentaerythritol diphosphite, diisodecyloxy pentaerythritol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite, bis(2,4,6-tris(tert-butylphenyl)pentaerythritol diphosphite, tristearyl sorbitol tri-phosphite, tetrakis(2,4-di-tert-butyl-phenyl) 4,4′-biphenylene diphosphonite, bis(2,4-di-tert-butyl-6-methylphenyl) methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite, 2,2′,2″-nitrilo[triethyl tris(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite], 2-ethylhexyl(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite and 5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane.

Combinations comprising more than one organophosphorous compound are contemplated. When used in combination the organo phosphorous compounds can be of the same type or different types. For example, a combination can comprise two phosphite or a combination can comprise a phosphite and a phosphonite. In some embodiments, phosphorus-containing stabilizers with a molecular weight greater than 300 are useful. Phosphorus-containing stabilizers, for example an aryl phosphite are usually present in the composition in an amount from 0.005 to 3 wt %, specifically 0.01 to 1.0 wt %, based on total weight of the composition.

Hindered phenols can also be used as antioxidants, for example alkylated monophenols, and alkylated bisphenols or poly phenols. Exemplary alkylated monophenols include 2,6-di-tert-butyl-4-methylphenol; 2-tert-butyl-4,6-dimethylphenol; 2,6-di-tert-butyl-4-ethylphenol; 2,6-di-tert-butyl-4-n-butylphenol; 2,6-di-tert-butyl-4-isobutylphenol; 2,6-dicyclopentyl-4-methylphenol; 2-(alpha-methylcyclohexyl)-4,6-dimethylphenol; 2,6-dioctadecyl-4-methylphenol; 2,4,6-tricyclohexylphenol; 2,6-di-tert-butyl-4-methoxymethylphenol; nonyl phenols which are linear or branched in the side chains, for example, 2,6-di-nonyl-4-methylphenol; 2,4-dimethyl-6-(1′-methylundec-1′-yl)phenol; 2,4-dimethyl-6-(1′-methylheptadec-1′-yl)phenol; 2,4-dimethyl-6-(1′-methyltridec-1′-yl)phenol or a combination comprising at least one of the foregoing. Exemplary alkylidene bisphenols include 2,2′-methylenebis(6-tert-butyl-4-methylphenol), 2,2′-methylenebis(6-tert-butyl-4-ethylphenol), 2,2′-methylenebis[4-methyl-6-(alpha-methylcyclohexyl)-phenol], 2,2′-methylenebis(4-methyl-6-cyclohexylphenol), 2,2′-methylenebis(6-nonyl-4-methylphenol), 2,2′-methylenebis(4,6-di-tert-butylphenol), 2,2′-ethylidenebis(4,6-di-tert-butylphenol), 2,2′-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2′-methylenebis[6-(alpha-methylbenzyl)-4-nonylphenol], 2,2′-methylenebis[6-(alpha, alpha-dimethylbenzyl)-4-nonylphenol], 4,4′-methylenebis-(2,6-di-tert-butylphenol), 4,4′-methylenebis(6-tert-butyl-2-methylphenol), 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydroxy-2-methyl-phenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis[3,3-bis(3′-tert-butyl-4′-hydroxyphenyl)butyrate], bis(3-tert-butyl-4-hydroxy-5-methyl-phenyl)dicyclopentadiene, bis[2-(3′-tert-butyl-2′-hydroxy-5′-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate, 1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis-(3,5-di-tert-butyl-4-hydroxyphenyepropane, 2,2-bis-(5-tert-butyl-4-hydroxy2-methylphenyl)-4-n-dodecylmercaptobutane, 1,1,5,5-tetra-(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane or a combination comprising at least one of the foregoing.

The hindered phenol compound can have a molecular weight of greater than 300 g/mole. The high molecular weight can help retain the hindered phenol moiety in the polymer melt at high processing temperatures, for example greater than 300° C. Hindered phenol stabilizers, are usually present in the composition in an amount from 0.005 to 2 wt %, specifically 0.01 to 1.0 wt %, based on total weight of the composition.

Examples of mold release agents include both aliphatic and aromatic carboxylic acids and their alkyl esters, for example, stearic acid, behenic acid, pentaerythritol tetrastearate, glycerin tristearate, and ethylene glycol distearate. Polyolefins such as high-density polyethylene, linear low-density polyethylene, low-density polyethylene and similar polyolefin homopolymers and copolymers can also be used a mold release agents. Mold release agents are typically present in the composition at 0.05 to 10 wt %, based on total weight of the composition, specifically 0.1 to 5 wt %. Preferred mold release agents will have high molecular weight, typically greater than 300, to prevent loss of the release agent from the molten polymer mixture during melt processing.

In particular, an optional polyolefin can be added to modify the chemical resistance characteristics and mold release characteristics of the composition. Homopolymers such as polyethylene, polypropylene, polybutene can be used either separately or in combination. Polyethylene can be added as high-density polyethylene (HDPE), low-density polyethylene (LDPE), or branched polyethylene. Polyolefins can also be used in copolymeric form with compounds containing carbonic acid groups such as maleic acid or citric acid or their anhydrides, acid compounds containing acrylic acid groups such as acrylic acid ester, and the like, as well as combinations comprising at least one of the foregoing. When present, the polyolefin, in particular HDPET, is used in an amount from more than 0 to 10 wt %, specifically 0.1 to 8 wt %, more specifically from 0.5 to 5 wt %, all based on the total weight of the composition.

In some embodiments, the polyetherimide compositions can further include at least one additional polymer. Examples of such additional polymers include and are not limited to PPSU (polyphenylene sulfone), polyetherimides, PSU (polysulfone), PPET (polyphenylene ether), PFA (perfluoroalkoxy alkane), MFA (co-polymer of TFE tetrafluoroethylene and PFVE perfluorinated vinyl ether), FEP (fluorinated ethylene propylene polymers), PPS (poly(phenylene sulfide), PTFE (polytetrafluoroethylene), PA (polyamide), PBI (polybenzimidazole) and PAI (poly(amide-imide)), poly(ether sulfone), poly(aryl sulfone), polyphenylenes, polybenzoxazoles, polybenzthiazoles, as well as blends and co-polymers thereof. When present, the polymer is used in an amount from more than 0 to 20 wt %, specifically 0.1 to 15 wt %, more specifically from 0.5 to 10 wt %, all based on the total weight of the composition. In some embodiments, no polymer other than the polyetherimide as described herein is present in the composition.

Colorants such as pigment and/or dye additives can also optionally be present. Useful pigments can include, for example, inorganic pigments such as metal oxides and mixed metal oxides such as zinc oxide, titanium dioxide, iron oxides, or the like; sulfides such as zinc sulfides, or the like; aluminates; sodium sulfo-silicates sulfates, chromates, or the like; carbon blacks; zinc ferrites; ultramarine blue; organic pigments such as azos, di-azos, quinacridones, perylenes, naphthalene tetracarboxylic acids, flavanthrones, isoindolinones, tetrachloroisoindolinones, anthraquinones, enthrones, dioxazines, phthalocyanines, and azo lakes; Pigment Red 101, Pigment Red 122, Pigment Red 149, Pigment Red 177, Pigment Red 179, Pigment Red 202, Pigment Violet 29, Pigment Blue 15, Pigment Blue 60, Pigment Green 7, Pigment Yellow 119, Pigment Yellow 147, Pigment Yellow 150, and Pigment Brown 24; or combinations comprising at least one of the foregoing pigments. Pigments are generally used in amount from 0 to 10 wt %, specifically 0 to 5 wt %, based on the total weight of the composition. In some instances, where improved impact is desired pigments such as titanium dioxide will have a mean particle size of less than 5 microns.

In some instances it is desired to have polyetherimide compositions that are essentially free of bromine and chlorine. “Essentially free” of bromine and chlorine means that the composition has less than 3 wt % of bromine and chlorine, and in other embodiments less than 1 wt % bromine and chlorine by weight of the composition. In other embodiments, the composition is halogen free. “Halogen free” is defined as having a halogen content (total amount of fluorine, bromine, chlorine, and iodine) of less than 1000 parts by weight of halogen per million parts by weight of the total composition (ppm). The amount of halogen can be determined by ordinary chemical analysis such as atomic absorption.

The polyetherimide compositions can be prepared by blending the ingredients under conditions for the formation of an intimate blend. Such conditions often include melt mixing in single or twin screw type extruders, mixing bowl, or similar mixing devices that can apply a shear to the components. Twin-screw extruders are often preferred due to their more intensive mixing capability and self-wiping capability, over single screw extruders. It is often advantageous to apply a vacuum to the blend through at least one vent port in the extruder to remove volatile impurities in the composition. Often it is advantageous to dry the PET and polyimide polymers prior to melting. The melt processing is often done at 290 to 340° C. to avoid excessive polymer degradation while still allowing sufficient melting to get an intimate polymer mixture free of any unbelted components. The polymer blend can also be melt filtered using a 40 to 100 micron candle or screen filter to remove undesirable black specks or other heterogeneous contaminants.

In an exemplary process, the various components are placed into an extrusion compounder to produce a continuous strand that is cooled and then chopped into pellets. In another procedure, the components are mixed by dry blending, and then fluxed on a mill and comminuted, or extruded and chopped. The composition and any optional components can also be mixed and directly molded, e.g., by injection or transfer molding techniques. Preferably, all of the components are freed from as much water as possible. In addition, compounding is carried out to ensure that the residence time in the machine is short; the temperature is carefully controlled; the friction heat is utilized; and an intimate blend between the components is obtained. The polyetherimide compositions can then be molded in any equipment conventionally used for polyetherimide compositions, such as a Newbury or van Dorn type injection-molding machine with conventional cylinder temperatures, at 250° C. to 320° C., and conventional mold temperatures at 55° C. to 120° C.

As discussed above, the polyetherimide compositions are formulated to have excellent electrical tracking resistance. In some embodiments, the compositions have number of drops to tracking at 250 volts greater than or equal to 50 drops, greater than or equal to 60 drops, greater than or equal to 70 drops, greater than or equal to 80 drops, greater than or equal to 90 drops, or greater than or equal to 100 drops, determined according to ASTM D-3638-85.

The polyetherimide compositions can further have a tensile strength of greater than or equal to 50 MPa (Mega Pascal), greater than or equal to 60 MPa, greater than or equal to 70 MPa, or greater than or equal to 80 MPa determined according to ASTM D638.

The polyetherimide compositions can further have a tensile modulus of greater than or equal to 6000 GPa (Giga Pascal), greater than or equal to 7000 GPa, greater than or equal to 8000 GPa, or greater than or equal to 10,000 GPa determined according to ASTM D638.

The polyetherimide compositions can further have a heat deflection temperature (HDT) of 190 to 230° C., more specifically 195 to 220° C., measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.

Shaped, formed, or molded articles comprising the polyetherimide compositions are also provided. The polyetherimide compositions can be molded into useful shaped articles by a variety of means such as injection molding, extrusion, rotational molding, blow molding, and thermoforming. Thus the polyetherimide compositions can be used to form a foamed article, a molded article, a thermoformed article, an extruded film, an extruded sheet, one or more layers of a multi-layer article (e.g. a cap-layer), a substrate for a coated article, or a substrate for a metallized article.

In another embodiment, at least one of the following articles are contained in or are derived from the compositions encompassed by this disclosure: a solar apparatus, an electrical junction box, an electrical connector, an electrical vehicle charger, an outdoor electrical enclosure, a smart meter enclosure, a smart grid power node, PV (photovoltaic) frame, and miniature circuit breaker (MCB) applications.

The polyetherimide compositions having improved CTI performance and balanced mechanical properties are further illustrated by the following non-limiting examples. All parts and percentages are by weight unless explicitly stated otherwise. All temperatures are degrees Celsius unless explicitly stated otherwise.

EXAMPLES

The materials used in the Examples are described in Table 1.

TABLE 1 Source, Component Chemical Description Vendor PEI Polyetherimide (ULTEM* 4001), P PTFE SABIC filled, standard flow Polyetherimide (Tg 217° C.) PEI2 Polyetherimide copolymer (ULTEM* 5001), SABIC transparent, standard flow (Tg 225° C.) PEI3 Polyetherimide sulfone copolymer SABIC (EXTEM* VH1003), (Tg 247° C.) PEI4 Polyetherimide sulfone copolymer SABIC (EXTEM*), transparent, enhanced flow (Tg 267° C.) PTFE Polytetrafluoroethylene Shamrock (Shamrock Fluoro T801) Technologies Jetfine Talc having a D95 of 3.5 microns IMERYS Talc 3CA HTP ultra- Particle size distribution (D95) - 4.5 microns Imifabi fine talc

Blending, Extrusion, and Molding Conditions

Compositions were formed by melt mixing the polyetherimide and fillers. Extrusion was carried out in a 2.5-inch twin screw, vacuum vented extruder. The extruder was set at about 300-350° C. The blends were run at approximately 250 rotations per minute (rpm) under vacuum. Compositions were made in a one pass method. The extrudate was cooled, pelletized, and dried at 150° C. Test samples were injection molded at a set temperature of 340-350° C. and mold temperature of 150-160° C. using a 30 second cycle time.

Testing Procedures

All molded samples were conditioned for at least 48 hours at 50% relative humidity prior to testing. Properties were measured using ASTM test methods. Unless specified to the contrary herein, all test standards are the most recent standard in effect at the time of filing this application.

Notched Izod impact values were measured at room temperature on 3.2 millimeter thick bars as per ASTM D256. Bars were notched prior to oven aging; samples were tested at room temperature. Results are in Joules per meter (J/m).

Tensile properties were measured on 3.2 millimeter type I bars as per ASTM method D638 at 23° C. with a crosshead speed of 5 millimeters/minute. Percent elongation (% Elongation) is reported at break (B). Tensile modulus, tensile strength at yield, tensile strength at break results is reported in MPa (Mega Pascal) or GPa (Giga Pascal).

Melt flow rates (MFR) were measured in accordance with ASTM D1238 at 337° C., using a 6.7 kilogram (kg) weight. MFR is reported in grams per 10 minutes (g/10 min).

Heat Deflection Temperature (HDT) was measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648. HDT is reported in degree Celsius (° C.).

Electrical tracking resistance tests were performed on a 3 mm square plaque (6×6 cm) in accordance with the ASTM D-3638. The test can be started at any given voltage. At each voltage 5 specimens are tested and the average number of drops is recorded. The test is performed at (at least) 4 different voltages, where there should be at least two data points with an average number of drops higher than 50 and two data points with an average number of drops lower than 50. A voltage extrapolation to 50 drops is made, and based on this voltage (V_(ASTM)) a PLC class is assigned. This assignment is provided according to the table below. The CTI rating of a polymer indicates how resistant the polymeric material is to electrical tracking at certain voltages. CTI ratings range from CTI-0 to CTI-5 with a CTI-1 rating indicating that a polymer is more resistant to electrical tracking than a polymer with a lower CTI rating (for example CTI-3).

VASTM PLC  <100 5 100-174 4 175-249 3 250-399 2 400-599 1 ≧600 0

A screening method was employed to predict the CTI-2 performance of polyetherimide compositions. The method employed the ASTM D-3638 method but testing was conducted at only one voltage, 250 V. The number of drops until failure was recorded and no more than 100 drops were applied. A prediction of a CTI-2 rating for a sample was based on reaching at least 50 drops of the electrolyte solution before failure at 250 V. A prediction of not receiving a CTI rating was based on failure before reaching 50 drops of the electrolyte solution at 250 V. The screening method for predicting CTI-2 rating is identified throughout the disclosure as the CTI test.

Examples 1-9

Examples 1-9 demonstrate the effect of the addition of talc having different size distributions to compositions containing polyetherimide and polytetrafluoroethylene on mechanical and CTI properties. Formulations and results are shown in table 2.

TABLE 2 1* 2* 3* 4 5 6 7* 8 9 Component PEI 90 81 76.5 67.5 58.5 54 60 67.5 58.5 PTFE 10 9.0 8.5 7.5 6.5 6.0 7.5 6.5 Jet fine Talc 3CA 0 10 15 25 35 40 40 HTP Ultrafine Talc 25 35 Property Tensile strength (MPa) 101 105 94 87 73 75 83 85 71 Tensile modulus (GPa) 3144 4517 5360 6997 9074 10113 5794 7563 9125 % Elongation 24 6 3 2 1 1 1 2 1 Flexural strength (GPa) 157.6 158 161 170 129 122 142 129 127 Flexural Modulus (MPa) 4718 4718 5542 4850 8656 9322 5873 7271 8403 Unnotched Impact strength (J/m) 529 480 366 249 239 178 189 260 233 MFR 337° C., 6.7 Kg, 5 min (g/10 min) 9.5 6.0 5.2 4.2 3.3 3.2 12 4.2 3.6 HDT (1.82 MPa) 200 194 196 201 202 205 200 201 204 No. of drops for tracking@ 250 Volts 5 7 19.6 93.4 100 100 25 77 100 Tracking Voltage 190 190 218 290 318 335 285 308 PLC rating 3 3 3 2 2 2 2 2 *Comparative Example

Comparative example 1 shows that the number of drops to tracking at 250 volts for a composition containing 90 wt % of PEI and 10 wt % of PTFE is only 5. When 10 wt % or 15 wt % of talc is added (comparative examples 2 and 3), the number of drops to tracking at 250 volts only shows slight improvement to 7 and 19.6 respectively. However, upon the addition of 25 wt % to 40 wt % of talc having different size distributions, the number of drops to tracking at 250 volts increases to greater than 50.

The results are surprising because the addition of 40 wt % of HTP ultrafine talc to PEI alone does not improve the CTI performance of PEI as the number of drops to tracking at 240 volts is only 25 failing the 50 drops test (comparative example 7). However, when 25 wt % or 35 wt % of HTP ultrafine talc is added to a combination of PEI and PTFE, the CTI performance of the composition is improved significantly passing the 50 drops CTI test (examples 8 and 9).

These examples demonstrate that compositions containing 25 wt % to 45 wt % of talc, 5 wt % to 8 wt % of PTFE, and 50 wt % to 70 wt % of polyetherimide achieve a combination of a tensile strength greater than or equal to 70 MPa, tensile modulus greater than equal to 7500 GPa, impact strength greater than or equal to 175 J/m, heat performance (HDT) greater than or equal to 200° C., number of drops to tracking at 250 volts greater than or equal to 50 drops, and tracking voltage greater than or equal to 250 volts.

Examples 10-13

Examples 10-13 demonstrate the effect of the addition of polytetrafluoroethylene to compositions containing polyetherimide and talc on mechanical and CTI properties. Formulations and results are shown in Table 3.

TABLE 3 10* 11 12* 13 Component PEI 75 67.5 75 67.5 PTFE 0 7.5 0 7.5 Jet fine Talc 3CA 25 25 HTP Ultrafine Talc 25 25 Property Tensile strength (MPa) 98 87 107 85 Tensile modulus (GPa) 8469 6997 6574 7563 % Elongation 2 2 4 2 Flexural strength (GPa) 154 170 185 129 Flexural Modulus (MPa) 9060 4850 6528 7271 Unnotched Impact strength (J/m) 297 249 790 260 MFR 337° C., 6.7 Kg, 5 min 8 4.2 10 4.2 (g/10 min) HDT (1.82 MPa) 205 201 200 201 No. of drops for tracking@ 6 93.4 25 100 250 Volts Tracking Voltage 226 290 220 285 PLC rating 3 2 3 2 *Comparative Example

These examples demonstrate that formulations containing 75 wt % of polyetherimide and 25 wt % of talc with D95 of 3.5 microns or 4.5 microns have number of drops to tracking at 250 volts of 6 and 25 respectively. When 7.5 wt % of PTFE is added, the number of drops to tracking at 250 volts is increased to 93.4 and 100 respectively. In addition, the PTFE-containing compositions also achieve a combination of a tensile strength greater than or equal to 80 MPa, a tensile modulus greater than or equal to 6500 GPa, a heat deflection temperature greater than or equal to 200° C., and a tracking voltage greater than or equal to 250 volts.

Examples 14-17

Examples 14-17 demonstrate the effect of the addition of various amounts of polytetrafluoroethylene to compositions containing polyetherimide and talc on mechanical and CTI properties. Formulations and results are shown in table 4.

TABLE 4 14 15* 16* 17* Component PEI 67.5 70 70 77.5 PTFE 7.5 5 10 7.5 Jet fine Talc 3CA 25 25 20 15 Property Tensile strength (MPa) 78 70 87 75 Tensile modulus (GPa) 7855 7517 6774 5468 % Elongation 2 1 3 2 Flexural strength (GPa) 164 132 159 153 Flexural Modulus (MPa) 7084 6720 6096 5176 Unnotched Impact strength (J/m) 429 143 440 529 MFR 337° C., 6.7 Kg, 5 min 7.4 6.8 8.4 10.3 (g/10 min) HDT (1.82 MPa) 201 200 195 194 No. of drops for tracking@ 93 13 21 12 250 Volts Tracking Voltage 257 236 229 207 PLC rating 2 3 3 3 *Comparative Example

These results show that compositions containing 20 wt % to 30 wt % of talc, greater than 5 wt % but less than 10 wt % of PTFE, and greater than 65 wt % but less than 72 wt % of PEI achieve the desired levels of tensile strength, impact strength, HDT, and CTI performance.

Examples 18-21

Examples 18-21 demonstrate the effect of the addition of talc to compositions containing a different type of polyetherimide and PTFE. Formulations and results are shown in table 5.

TABLE 5 18* 19* 20* 21 Component PEI2 70 60 50 50 PTFE 10 Jet fine Talc 3CA 30 40 50 40 Property Tensile strength (MPa) 73 70 36 53 Tensile modulus (GPa) 9574 11291 14048 10340 % Elongation 1 1 2 2 Flexural strength (GPa) 112 111 99 83 Flexural Modulus (MPa) 9282 9769 12221 8796 Unnotched Impact strength (J/m) 142 140 76 93 MFR 337° C., 6.7 Kg, 5 min 4 3 1 2 (g/10 min) HDT (1.82 MPa) 206 206 207 203 No. of drops for tracking at 23 100 100 100 250 Volts Tracking Voltage 232 285 366 311 PLC rating 3 2 2 2 *Comparative Example

Comparative example 18 shows that the number of drops to tracking at 250 volts for a composition containing 70 wt % of PEI2 and 30 wt % of talc is only 23. When the amount of talc is increased to 40 wt % or 50 wt %, (comparative examples 19 and 20), the number of drops to tracking at 250 volts increases to 100. However, the addition of increased amount of talc can compromise the tensile strength and flexural strength of the composition. When the polyetherimide composition contains PTFE, less talc is needed in order to pass the 50 drops CTI test. Example 21 shows that the addition of PTFE together with talc to PEI2 results in a composition having a combination of a tensile strength greater than or equal to 50 MPa, tensile modulus greater than equal to 10.00 GPa, impact strength greater than or equal to 90 J/m, HDT greater than or equal to 200° C., number of drops to tracking at 250 volts greater than or equal to 50 drops, and tracking voltage greater than or equal to 300 volts.

Examples 22-25

Examples 22-25 demonstrate the effect of the addition of polytetrafluoroethylene to compositions containing polyetherimide sulfone and talc. Formulations and results are shown in Table 6.

TABLE 6 22* 23* 24* 25 Component PEI3 70 60 50 50 PTFE 10 Jet fine Talc 3CA 30 40 50 40 Property Tensile strength (MPa) 61 49 40 48 Tensile modulus (GPa) 11576 11248 13008 11274 % Elongation 1 1 2 1 Flexural strength (GPa) 96 82 94 72 Flexural Modulus (MPa) 9445 9877 12362 9694 Unnotched Impact strength (J/m) 181 57 54 66 MFR 337° C., 6.7 Kg, 5 min 12 8 3 4 (g/10 min) HDT (1.82 MPa) 214 214 216 212 No. of drops for tracking@ 7 100 100 100 250 Volts Tracking Voltage 212 278 379 347 PLC rating 3 2 2 2 *Comparative Example

These examples show that combining 40 wt % or 50 wt % of talc with polyetherimide sulfone PEI3 and PTFE can achieve balanced mechanical and CTI properties.

Examples 26-29

Examples 26-29 demonstrate the effect of the addition of talc and PTFE to polyetherimide sulfone PEI4 on mechanical and CTI properties. Formulations and results are shown in table 7.

TABLE 7 26* 27 28 29 Component PEI4 70 60 50 50 PTFE 10 Jet fine Talc 3CA 30 40 50 40 Property Tensile strength (MPa) 68 48 45 42 Tensile modulus (GPa) 7903 11031 11450 11016 % Elongation 1 1 1 1 Flexural strength (GPa) 107 73 71 68 Flexural Modulus (MPa) 7835 9627 11650 9286 Unnotched Impact strength (J/m) 67 56 40 MFR 337° C., 6.7 Kg, 5 min 9 5 3 3 (g/10 min) HDT (1.82 MPa) 215 218 218 215 No. of drops for tracking@ 12 91 100 100 250 Volts Tracking Voltage 190 286 312 343 PLC rating 3 2 2 2 *Comparative Example

Comparative example 26 shows that the number of drops to tracking at 250 volts for a composition containing 70 wt % of PEI4 and 30 wt % of talc is only 23. When the amount of talc is increased to 40 wt % or 50 wt %, the number of drops to tracking at 250 volts increases to 91 and 100 respectively. When PTFE is present, only 40 wt % of talc is needed in order to increase the number of drops to tracking at 250 volts to 100. The PTFE-containing composition also has balanced mechanical properties.

Set forth below are specific embodiments of polyetherimide compositions, methods of manufacture and articles comprising the same.

In an embodiment, a composition comprises, based on the total weight of the composition, 45 wt % to 75 wt % of a polyetherimide; and 20 wt % to 45 wt % of talc; and 5 wt % to 15 wt % of a fluorinated polymer such as polytetrafluoroethylene; wherein the composition has a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85.

The polyetherimide comprises units of the formula (1) wherein R is the same or different, and is a substituted or unsubstituted divalent organic group, T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions; and wherein Z is an aromatic C₆₋₂₄ monocyclic or polycyclic moiety optionally substituted with 1 to 6 C₁₋₈ alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded, preferably R is a divalent group of the formula (2) wherein Q¹ is —O—, —S—, —C(O)—, —SO₂—, —SO—, —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof, or —(C₆H₁₀)_(z)— wherein z is an integer from 1 to 4, and Z is a divalent group of the formula (3a), wherein Q is —O—, —S—, —C(O)—, —SO₂—, —SO—, or —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof, more preferably R is m-phenylene and Q is isopropylidene, and in an embodiment, at least 50 mole percent (mol %) of the R groups are bis(3,4′-phenylene)sulfone, bis(3,3′-phenylene)sulfone, or a combination comprising at least one of the foregoing and the remaining R groups are p-phenylene, m-phenylene or a combination comprising at least one of the foregoing; and Z is 2,2-(4-phenylene)isopropylidene.

An exemplified composition comprises, based on the total weight of the composition, 50 wt % to 70 wt % of a polyetherimide; and 25 wt % to 45 wt % of talc; and 5 wt % to 8 wt % of polytetrafluoroethylene; wherein the composition has: a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85; and a tacking voltage of greater than or equal to 250 volts according to ASTM D-3638-85. Optionally, the composition has: a tensile strength greater than or equal to 70 MPa determined according to ASTM D638; a tensile modulus of greater than or equal to 6500 GPa determined according to ASTM method D638, and a heat deflection temperature of greater than or equal to 200° C. measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.

Another exemplified composition comprises, based on the total weight of the composition, 45 wt % to 55 wt % of a polyetherimide sulfone; and 35 wt % to 45 wt % of talc; and 8 wt % to 15 wt % of polytetrafluoroethylene; wherein the composition has: a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85; and a tacking voltage of greater than or equal to 300 volts according to ASTM D-3638-85, wherein the polyetherimide sulfone comprises units of the formula (1) wherein R is a divalent group of the formula

wherein Q¹ is —SO₂—, and T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions; and wherein Z is an aromatic C₆₋₂₄ monocyclic or polycyclic moiety optionally substituted with 1 to 6 C₁₋₈ alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded. Optionally the composition has: a tensile strength greater than or equal to 40 MPa determined according to ASTM D638; a tensile modulus of greater than or equal to 11,000 GPa determined according to ASTM method D638, and a heat deflection temperature of greater than or equal to 210° C. measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.

The composition of any one of the foregoing embodiments can optionally further comprise an additive an additive selected from a processing aid, a heat stabilizer, a dye, a flame retardant, or a combination comprising at least one of the foregoing.

In another embodiment, an insulating material comprises the composition of any one of foregoing embodiments.

Also disclosed is an article selected from a molded article, a thermoformed article, an extruded film, an extruded sheet, one or more layers of a multi-layer article, a substrate for a coated article, and a substrate for a metallized article made from the composition of any one of the foregoing embodiments.

A method of manufacture of an article comprises molding, extruding, or casting the composition of any one of the foregoing embodiments to form the article.

A method of controlling the tracking of an electrical current of an article of manufacture comprises: providing a composition of any one of the foregoing embodiments and processing the composition to form an article of manufacture.

For any of the foregoing articles or methods, the article can be a solar apparatus, an electrical junction box, an electrical connector, an electrical vehicle charger, an outdoor electrical enclosure, a smart meter enclosure, a smart grid power node, a photovoltaic frame and a miniature circuit breaker.

The singular forms “a”, “an”, and “the” include plural referents unless the context clearly dictates otherwise. “Or” means “and/or”. The endpoints of all ranges directed to the same component or property are inclusive and independently combinable. Unless defined otherwise, technical and scientific terms used herein have the same meaning as is commonly understood by one of skill in the art to which this invention belongs.

As used herein, a “combination” is inclusive of blends, mixtures, alloys, reaction products, and the like. Compounds are described using standard nomenclature. For example, any position not substituted by any indicated group is understood to have its valency filled by a bond as indicated, or a hydrogen atom. A dash (“-”) that is not between two letters or symbols is used to indicate a point of attachment for a substituent. For example, —CHO is attached through carbon of the carbonyl group.

The term “alkyl” includes branched or straight chain, unsaturated aliphatic C₁₋₃₀ hydrocarbon groups e.g., methyl, ethyl, n-propyl, i-propyl, n-butyl, s-butyl, t-butyl, n-pentyl, s-pentyl, n- and s-hexyl, n- and s-heptyl, and, n- and s-octyl. “Alkenyl” means a straight or branched chain, monovalent hydrocarbon group having at least one carbon-carbon double bond (e.g., ethenyl (—HC═CH₂)). “Alkoxy” means an alkyl group that is linked via an oxygen (i.e., alkyl-O—), for example methoxy, ethoxy, and sec-butyloxy groups. “Alkylene” means a straight or branched chain, saturated, divalent aliphatic hydrocarbon group (e.g., methylene (—CH₂—) or, propylene (—(CH₂)₃—)). “Cycloalkylene” means a divalent cyclic alkylene group, —C_(n)H_(2n-x), wherein x represents the number of hydrogens replaced by cyclization(s). “Aryl” means an aromatic hydrocarbon group containing the specified number of carbon atoms, such as to phenyl, tropone, indanyl, or naphthyl. The prefix “hetero” means that the compound or group includes at least one ring member that is a heteroatom (e.g., 1, 2, or 3 heteroatom(s)), wherein the heteroatom(s) is each independently N, O, S, or P.

“Substituted” means that the compound or group is substituted with at least one (e.g., 1, 2, 3, or 4) substituents instead of hydrogen, where each substituent is independently nitro (—NO₂), cyano (—CN), hydroxy (—OH), halogen, thiol (—SH), thiocyano (—SCN), C₁₋₆ alkyl, C₂₋₆ alkenyl, C₂₋₆ alkynyl, C₁₋₆ haloalkyl, C₁₋₉ alkoxy, C₁₋₆ haloalkoxy, C₃₋₁₂ cycloalkyl, C₅₋₁₈ cycloalkenyl, C₆₋₁₂ aryl, C₇₋₁₃ arylalkylene (e.g., benzyl), C₇₋₁₂ alkylarylene (e.g., toluyl), C₄₋₁₂ heterocycloalkyl, C₃₋₁₂ heteroaryl, C₁₋₆ alkyl sulfonyl (—S(═O)₂-alkyl), C₆₋₁₂ arylsulfonyl (—S(═O)₂-aryl), or tosyl (CH₃C₆H₄SO₂—), provided that the substituted atom's normal valence is not exceeded, and that the substitution does not significantly adversely affect the manufacture, stability, or desired property of the compound. When a compound is substituted, the indicated number of carbon atoms is the total number of carbon atoms in the group, including those of the substituent(s).

All references cited herein are incorporated by reference in their entirety. While typical embodiments have been set forth for the purpose of illustration, the foregoing descriptions should not be deemed to be a limitation on the scope herein. Accordingly, various modifications, adaptations, and alternatives can occur to one skilled in the art without departing from the spirit and scope herein. 

1. A composition comprising, based on the total weight of the composition, 45 wt % to 75 wt % of a polyetherimide; and 20 wt % to 45 wt % of talc; and 5 wt % to 15 wt % of a fluorinated polymer; wherein the composition has a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85.
 2. The composition of claim 1, wherein the polyetherimide comprises units of the formula

wherein R is the same or different, and is a substituted or unsubstituted divalent organic group, T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions; and wherein Z is an aromatic C₆₋₂₄ monocyclic or polycyclic moiety optionally substituted with 1 to 6 C₁₋₈ alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded.
 3. The composition of claim 1, wherein R is a divalent group of the formula

wherein Q¹ is —O—, —S—, —C(O)—, —SO₂—, —SO—, —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof, or —(C₆H₁₀)_(z)— wherein z is an integer from 1 to 4, and Z is a divalent group of the formula

wherein Q is —O—, —S—, —C(O)—, —SO₂—, —SO—, or —C_(y)H_(2y)— wherein y is an integer from 1 to 5 or a halogenated derivative thereof.
 4. The composition of claim 3, wherein R is m-phenylene and Q is isopropylidene.
 5. The composition of claim 3, wherein at least 50 mole percent (mol %) of the R groups are bis(3,4′-phenylene)sulfone, bis(3,3′-phenylene)sulfone, or a combination comprising at least one of the foregoing and the remaining R groups are p-phenylene, m-phenylene or a combination comprising at least one of the foregoing; and Z is 2,2-(4-phenylene)isopropylidene.
 6. The composition of claim 1, wherein the fluorinated polymer comprises polytetrafluoroethylene.
 7. The composition of claim 1 comprising, based on the total weight of the composition, 50 wt % to 70 wt % of a polyetherimide; and 25 wt % to 45 wt % of talc; and 5 wt % to 8 wt % of polytetrafluoroethylene; wherein the composition has: a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85; and a tracking voltage of greater than or equal to 250 volts according to ASTM D-3638-85.
 8. The composition of claim 7, wherein the composition has: a tensile strength greater than or equal to 70 MPa determined according to ASTM D638; a tensile modulus of greater than or equal to 6500 GPa determined according to ASTM method D638, and a heat deflection temperature of greater than or equal to 200° C. measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.
 9. The composition of claim 1 comprising, based on the total weight of the composition, 45 wt % to 55 wt % of a polyetherimide sulfone; and 35 wt % to 45 wt % of talc; and 8 wt % to 15 wt % of polytetrafluoroethylene; wherein the composition has: a number of drops to tracking at 250 volts of greater than or equal to 50 drops according to ASTM D-3638-85; and a tracking voltage of greater than or equal to 300 volts according to ASTM D-3638-85, wherein the polyetherimide sulfone comprises units of the formula

wherein R is a divalent group of the formula

wherein Q¹ is —SO₂—, and T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions; and wherein Z is an aromatic C₆₋₂₄ monocyclic or polycyclic moiety optionally substituted with 1 to 6 C₁₋₈ alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded.
 10. The composition of claim 9, wherein the composition has: a tensile strength greater than or equal to 40 MPa determined according to ASTM D638; a tensile modulus of greater than or equal to 11,000 GPa determined according to ASTM method D638, and a heat deflection temperature of greater than or equal to 210° C. measured on 3.2 millimeter injection molded bar at 1.82 MPa stress according to ASTM D648.
 11. The composition of claim 1, further comprising an additive selected from a processing aid, a heat stabilizer, a dye, a flame retardant, or a combination comprising at least one of the foregoing.
 12. An insulating material comprising the composition of claim
 1. 13. An article selected from a molded article, a thermoformed article, an extruded film, an extruded sheet, one or more layers of a multi-layer article, a substrate for a coated article, and a substrate for a metallized article made from the composition of claim
 1. 14. An article made from the composition of claim 1, wherein the article is a solar apparatus, an electrical junction box, an electrical connector, an electrical vehicle charger, an outdoor electrical enclosure, a smart meter enclosure, a smart grid power node, a photovoltaic frame and a miniature circuit breaker.
 15. A method of manufacture of an article, comprising molding, extruding, or casting the composition of claim 1 to form the article.
 16. A method of controlling the tracking of an electrical current of an article of manufacture, the method comprising: providing a composition of claim 1, and processing the composition to form an article of manufacture.
 17. The method of claim 16, wherein the article is a solar apparatus, an electrical junction box, an electrical connector, an electrical vehicle charger, an outdoor electrical enclosure, a smart meter enclosure, a smart grid power node, a photovoltaic frame and a miniature circuit breaker. 